Effects of bismuth on the matrix structure of ductile iron castings
U: Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019. / Stavrev, Dimitar (ur.). Pleven: Scientific-Technical Union of Mechanical Engineering, 2019. str. 8-10. urn:nbn:hr:115:062237
Glavaš, Zoran; Štrkalj, Anita

Citirajte ovaj rad

Glavaš, Z. i Štrkalj, A. (2019). Effects of bismuth on the matrix structure of ductile iron castings. U D. Stavrev, (Ur.), Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019 (str. 8-10). Pleven: Scientific-Technical Union of Mechanical Engineering. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:115:062237

Glavaš, Zoran i Anita Štrkalj. "Effects of bismuth on the matrix structure of ductile iron castings." Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019, Ur. Dimitar Stavrev, Scientific-Technical Union of Mechanical Engineering, 2019, str. 8-10. https://urn.nsk.hr/urn:nbn:hr:115:062237

Glavaš, Zoran i Anita Štrkalj. "Effects of bismuth on the matrix structure of ductile iron castings." U Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019, 8-10. Pleven: Scientific-Technical Union of Mechanical Engineering, 2019. Citirano 14.04.2024.. https://urn.nsk.hr/urn:nbn:hr:115:062237

Glavaš, Z. i Štrkalj, A. (2019) 'Effects of bismuth on the matrix structure of ductile iron castings', u Stavrev, D. (ur.), Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019, Scientific-Technical Union of Mechanical Engineering, Pleven, str. 8-10. Preuzeto s: https://urn.nsk.hr/urn:nbn:hr:115:062237 (Datum pristupa: 14.04.2024.)

Glavaš Z, Štrkalj A. Effects of bismuth on the matrix structure of ductile iron castings. U: D. Stavrev, ur. Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019. Pleven: Scientific-Technical Union of Mechanical Engineering; 2019. Str. 8-10. [pristupljeno 14.04.2024.] Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:062237

Z. Glavaš i A. Štrkalj, "Effects of bismuth on the matrix structure of ductile iron castings", Proceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019, D. Stavrev, Ur. Pleven: Scientific-Technical Union of Mechanical Engineering, 2019. [Online] Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:062237 [Citirano: 14.04.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:115:062237
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)Effects of bismuth on the matrix structure of ductile iron castings
AutorZoran Glavaš
AutorAnita Štrkalj
UrednikDimitar Stavrev
Autorova ustanovaSveučilište u Zagrebu
Metalurški fakultet
(Zavod za procesnu metalurgiju)
(Laboratorij za kemiju (opća, anorganska, fizikalna))
Autorova ustanovaSveučilište u Zagrebu
Metalurški fakultet
(Zavod za procesnu metalurgiju)
(Laboratorij za željezo, čelik i ljevarstvo)
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Metalurgija
Procesna metalurgija
Sažetak (engleski)
This paper deals with the effects of the addition of 0.00031, 0.00064, 0.001 and 0.0042 wt.% Bi on the matrix structure of ductile iron castings consisting of 7 sections of different thicknesses (3, 12, 25, 38, 50, 75 and 100 mm) and contain low content of Si (2.11 wt.%) and pearlite promoting element (0.018 wt.% Cu, 0.0055 wt.% Sn, 0.00041 wt.% Sb, 0.098 wt.% Mn). The Bi contents of 0.00031, 0.00064 and 0.001 wt.% were not significantly affected the share of ferrite and pearlite in the section thicknesses of 12, 25, 38, 50, 75 and 100 mm compared to the casting which does not contain Bi. In all these sections the share of pearlite was increased and the share of ferrite was decreased by the addition of 0.0042 wt.% Bi. All of the above-mentioned Bi contents were resulted in the formation of iron carbides in the section thickness of 3 mm. The share of carbides increases with increasing Bi content.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran - međunarodna recenzija
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov zbornikaProceedings book of the XXVIth International Scientific and Technical Conference Foundry 2019
Brojčani podacistr. 8-10
p-ISSN2535-017X
URN:NBNurn:nbn:hr:115:062237
Datum objave publikacije2019
SkupNaziv: XXVI International Scientific and Technical Conference Foundry 2019
Kratica: -
Lokacija: Pleven, Bugarska
Datum početka: 2019-04-10
Datum završetka: 2019-04-12
Vrsta izlaganja: Postersko izlaganje
URL dokumentahttp://bib.irb.hr/996725
Vrsta resursaTekst
IzdavačScientific-Technical Union of Mechanical Engineering
Mjesto izdavanjaPleven
Prava pristupaZatvoreni pristup
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2019-07-09 08:07:09